Stochastic Simulation of Mudcrack Damage Formation in an Environmental Barrier Coating

The FEAMAC/CARES program, which integrates finite element analysis (FEA) with the MAC/GMC (Micromechanics Analysis Code with Generalized Method of Cells) and the CARES/Life (Ceramics Analysis and Reliability Evaluation of Structures / Life Prediction) programs, was used to simulate the formation of mudcracks during the cooling of a multilayered environmental barrier coating (EBC) deposited on a silicon carbide substrate. FEAMAC/CARES combines the MAC/GMC multiscale micromechanics analysis capability (primarily developed for composite materials) with the CARES/Life probabilistic multiaxial failure criteria (developed for brittle ceramic materials) and Abaqus (Dassault Systèmes) FEA. In this report, elastic modulus reduction of randomly damaged finite elements was used to represent discrete cracking events. The use of many small-sized low-aspect-ratio elements enabled the formation of crack boundaries, leading to development of mudcrack-patterned damage. Finite element models of a disk-shaped three-dimensional specimen and a twodimensional model of a through-the-thickness cross section subjected to progressive cooling from 1,300 °C to an ambient temperature of 23 °C were made. Mudcrack damage in the coating resulted from the buildup of residual tensile stresses between the individual material constituents because of thermal expansion mismatches between coating layers and the substrate. A two-parameter Weibull distribution characterized the coating layer stochastic strength response and allowed the effect of the Weibull modulus on the formation of damage and crack segmentation lengths to be studied. The spontaneous initiation of cracking and crack coalescence resulted in progressively smaller mudcrack cells as cooling progressed, consistent with a fractal-behaved fracture pattern. Other failure modes such as delamination, and possibly spallation, could also be reproduced. The physical basis assumed and the heuristic approach employed, which involves a simple stochastic cellular automaton methodology to approximate the crack growth process, are described. The results ultimately show that a selforganizing mudcrack formation can derive from a Weibull distribution that is used to describe the stochastic strength response of the bulk brittle ceramic material layers of an EBC.

Nemeth, Noel N.↗
NASA NTRS2019

Fatigue Behavior of Coated Titanium Alloys

Advanced multi-component TiAlCrTaSiN-based multilayered coatings were developed and processed onto Ti-6Al-4V (Ti-6-4) and GammaMet PX (GMPX or TiAl) alloys by a magnetron-enhanced physical vapor deposition technique. The coatings have recently been in development with the goal of improving advanced titanium alloy, turbine engine component durability and oxidation-erosion resistance. In this work, the performance of the multi-component coating system (including the outer layer nitride based coating and inner TiAlCrSi oxidation barrier bond coat) was studied, and the coating's influence on the fatigue behavior of the titanium-based alloys were compared. Although the multi-component coating was initially optimized to improve the coating's high temperature oxidation and erosion resistance, the lower ductility nitride-based coating needs further work on microstructure or composition to improve its mechanical stress resistance and strain tolerance for use in cyclically loaded, turbine blade operating conditions. This is particularly true for GMPX and other γ-TiAl alloys because these intermetallic titanium alloys have limited ductility and are very sensitive to defects such as coating cracks. However, the inner layer TiAlCrSi-coating had better adhesion and ductility, and may be a suitable choice to improve the oxidation resistance of titanium alloys.

Oxidation Barrier Coatings↗
NASA NTRS2018

Microscale Fracture Testing of HfO2-Si Environmental Barrier Coatings

Environmental barrier coatings (EBCs) play a vital role in protecting advanced turbine components constructed from ceramic matrix composites. EBC performance is evaluated based on many factors such as mechanical and thermal properties and chemical stability. This study focuses on the mechanical properties of individual phases within a HfO2-Si EBC through the combined use of chevron-notched microcantilevers and finite element modeling. The Si- and HfO2-rich phases were found to have fracture toughness K(sub IC) values of 1.36+/-0.07 MPa·m1/2 and 1.99+/-0.36 MPa·m1/2, respectively. Despite irregular notch geometry, calculated K(sub IC) values agreed reasonably with literature values of monolithic samples for the respective phases. The relatively large scatter in the HfO2-rich samples is attributed to heterogeneity in fracture feature size and distribution of the HfO2 and HfSiO4 phases. Comparisons with bulk single-edge V-notched beams suggest bulk behavior is dictated by the fracture behavior of the Sirich phase with no contribution from the HfO2-rich phase.

Robertson, Andrew L.↗
NASA NTRS2018

Temperature Mapping Above and Below Air Film-Cooled Thermal Barrier Coatings Using Phosphor Thermometry

Thermal barrier coatings (TBCs) are typically used in conjunction with air film cooling to maximize overall cooling effectiveness and reliability while minimizing sacrifices in engine performance. The effects of thermal barrier coating (TBC) thermal protection and air film cooling effectiveness have usually been studied separately; however, their contributions to combined cooling effectiveness are interdependent and are not simply additive. The combined cooling effectiveness is always less than the sum of the cooling effectiveness of stand-alone TBC protection and stand-alone air film cooling. These diminishing returns arise because adding the thermally insulating TBC between the cooling air and the surface to be cooled reduces the air film cooling effectiveness and because the air film cooling reduces the heat flux through the TBC and therefore reduces the temperature difference sustained across the TBC thickness. Due to these considerations, combined cooling effectiveness must be measured to achieve an optimum balance between TBC thermal protection and air film cooling. In this investigation, temperature mapping above and below air film-cooled TBCs was performed using luminescence lifetime imaging-based phosphor thermometry. Measurements were performed in the NASA GRC Mach 0.3 burner rig on a TBC-coated plate using a scaled-up cooling hole geometry where both the hot mainstream gas temperature and the blowing ratio were varied. Surface temperature maps were obtained from a Cr-doped GdAlO3 thermographic phosphor deposited on the surface of the electron-beam vapor-deposited yttria-stabilized zirconia (YSZ) TBC. From separate plates, temperature maps from the bottom of the TBC were obtained from a thin Er-doped YSZ layer integrated into the TBC below the overlying undoped YSZ. Procedures for temperature and cooling effectiveness mapping above and below the air film-cooled TBC surface are described. Most importantly, these measurements enable mapping the combined cooling effectiveness below the TBC, which is more important than surface cooling effectiveness when there is a barrier coating between the hot mainstream gas and the surface that needs thermal protection. Advantages of the luminescence lifetime imaging method over infrared thermography, as well as its limitations to steady-state conditions are discussed.

cooling effectiveness.↗
NASA NTRS2018

Aerospace Ceramic Materials: Thermal, Environmental Barrier Coatings and SiC/SiC Ceramic Matrix Composites for Turbine Engine Applications

Ceramic materials play increasingly important roles in aerospace applications because ceramics have unique properties, including high temperature capability, high stiffness and strengths, excellent oxidation and corrosion resistance. Ceramic materials also generally have lower densities as compared to metallic materials, making them excellent candidates for light-weight hot-section components of aircraft turbine engines, rocket exhaust nozzles, and thermal protection systems for space vehicles when they are being used for high-temperature and ultra-high temperature ceramics applications. Ceramic matrix composites (CMCs), including non-oxide and oxide CMCs, are also recently being incorporated in gas turbine engines for high pressure and high temperature section components and exhaust nozzles. However, the complexity and variability of aerospace ceramic processing methods, compositions and microstructures, the relatively low fracture toughness of the ceramic materials, still remain the challenging factors for ceramic component design, validation, life prediction, and thus broader applications. This ceramic material section paper presents an overview of aerospace ceramic materials and their characteristics. A particular emphasis has been placed on high technology level (TRL) enabling ceramic systems, that is, turbine engine thermal and environmental barrier coating systems and non-oxide type SiC/SiC CMCs. The current status and future trend of thermal and environmental barrier coatings and SiC/SiC CMC development and applications are described.

Thermal Barrier Coatings↗
NASA NTRS2018

Oxidation Study of an Ultra High Temperature Ceramic Coatings Based on HfSiCN

High temperature fiber-reinforced ceramic matrix composites (CMCs) are important for aerospace applications because of their low density, high strength, and significantly higher-temperature capabilities compared to conventional metallic systems. The use of the SiCf/SiC and Cf/SiC CMCs allows the design of lighter-weight, more fuel efficient aircraft engines and also more advanced spacecraft airframe thermal protection systems. However, CMCs have to be protected with advanced environmental barrier coatings when they are incorporated into components for the harsh environments such as in aircraft engine or spacecraft applications. In this study, high temperature oxidation kinetics of an advanced HfSiCN coating on Cf/SiC CMC substrates were investigated at 1300 C, 1400 C, and 1500 C by using thermogravimetric analysis (TGA). The coating oxidation reaction parabolic rate constant and activation energy were estimated from the experimental results. The oxidation reaction studies showed that the coatings formed the most stable, predominant HfSiO4-HfO2 scales at 1400 C. A peroxidation test at 1400 C then followed by subsequent oxidation tests at various temperatures also showed more adherent scales and slower scale growth because of reduced the initial transient oxidation stage and increased HfSiO4-HfO2 content in the scales formed on the HfSiCN coatings.

Ultra High Temperature Ceramics (UHTC)↗
NASA NTRS2018

Performance and Durability of Advanced Environmental Barrier Coating Systems

This paper summarizes recent NASA environmental barrier coating (EBC) material advances for protecting the SiC/SiC Ceramic Matrix Composites (CMCs) for meeting next generation turbine engine performance requirements. We particularly present an advanced multicomponent rare earth silicate EBCs with HfO2-Si bond coat system, the temperature capability, environmental stability, and thermomechanical durability, advanced laboratory testing toward subelement demonstrations. Fundamental coating properties of the coating system will also be discussed, with the emphasis on the coating diffusion barrier performance and Calcium Magnesium Alumino-Silicate (CMAS) resistance.

Zhu, Dongming↗
NASA NTRS2018

Simulation of Stochastic Mud-Crack Damage Formation in an Environmental Barrier Coating

The integrated Finite Element Analysis–Micromechanics Analysis Code/Ceramics Analysis and Reliability Evaluation of Structures (FEAMAC/CARES) program was used to simulate the formation of mudflat-cracks from thermomechanical loading on a multi-layered Environmental Barrier Coating (EBC) system deposited on a ceramic substrate. FEAMAC/CARES combines MAC/GMC multiscale composite micromechanics code with CARES/Life probabilistic multiaxial failure criteria code and Abaqusfinite element analysis. In this work, step function elastic modulus reduction of randomly damaged finite elements was used to represent discrete cracking events. The use of many small-sized low-aspect-ratio finite elements enabled the depiction of crack boundaries and formation of mudflat patterned damage. Demonstrated examples include finite element models of button–sized disk–shaped 3-D specimen, and a 2-D model of through-the-thickness cross-section. All models were subjected to a progressive cool down from 1300oC to room temperature. Mudflat crack damage in the coating system resulted from the buildup of residual tensile stresses between the individual material constituents from thermal expansion mismatch. A 2-parameter Weibull distribution characterized the coating layer stochastic strength response and the effect of the Weibull modulus on the formation of damage was studied here.

residual tensile stress↗
NASA NTRS2018

Oxidation Study of an Ultra High Temperature Ceramic Coatings Based on HfSiCN

High temperature fiber-reinforced ceramic matrix composites (CMCs) are important for aerospace applications because of their low density, high strength, and significantly higher-temperature capabilities compared to conventional metallic systems. The use of the SiCf/SiC and Cf/SiC CMCs allows the design of lighter-weight, more fuel efficient aircraft engines and also more advanced spacecraft airframe thermal protection systems. However, CMCs have to be protected with advanced environmental barrier coatings when they are incorporated into components for the harsh environments such as in aircraft engine or spacecraft applications. In this study, high temperature oxidation kinetics of an advanced HfSiCN coating on Cf/SiC CMC substrates were investigated at 1300 C, 1400 C, and 1500 C by using thermogravimetric analysis (TGA). The coating oxidation reaction parabolic rate constant and activation energy were estimated from the experimental results. The oxidation reaction studies showed that the coatings formed the most stable, predominant HfSiO4-HfO2 scales at 1400 C. A peroxidation test at 1400 C then followed by subsequent oxidation tests at various temperatures also showed more adherent scales and slower scale growth because of reduced the initial transient oxidation stage and increased HfSiO4-HfO2 content in the scales formed on the HfSiCN coatings.

Environmental Barrier Coatings↗
NASA NTRS2018

Advanced Environmental Barrier Coating and SA Tyrannohex SiC Composites Integration for Improved Thermomechanical and Environmental Durability

The development of 2700 degF capable environmental barrier coating (EBC) systems, particularly, the Rare Earth "Hafnium" Silicon bond coat systems, have significantly improved the temperature capability and environmental stability of SiC/SiC Ceramic Matrix Composite Systems. We have specifically developed the advanced 2700 degF EBC systems, integrating the EBC to the high temperature SA Tyrannohex SiC fiber composites, for comprehensive performance and durability evaluations for potential turbine engine airfoil component applications. The fundamental mechanical properties, environmental stability and thermal gradient cyclic durability performance of the EBC - SA Tyrannohex composites were investigated. The paper will particularly emphasize the high pressure combustion rig recession, cyclic thermal stress resistance and thermomechanical low cycle fatigue testing of uncoated and environmental barrier coated Tyrannohex SiC SA composites in these simulated turbine engine combustion water vapor, thermal gradients, and mechanical loading conditions. We have also investigated high heat flux and flexural fatigue degradation mechanisms, determined the upper limits of operating temperature conditions for the coated SA composite material systems in thermomechanical fatigue conditions. Recent progress has also been made by using the self-healing rare earth-silicon based EBCs, thus enhancing the SA composite hexagonal fiber columns bonding for improved thermomechanical and environmental durability in turbine engine operation environments. More advanced EBC- composite systems based on the new EBC-Fiber Interphases will also be discussed.

Tyrannohex SiC Ceramics↗
NASA NTRS2018

Oxidation Study of an Ultra High Temperature Ceramic Coatings Based on HfSICN

High temperature fiber-reinforced ceramic matrix composites (CMCs) are important for aerospace applications because of their low density, high strength, and significantly higher-temperature capabilities compared to conventional metallic systems. The use of the SiC(sub f)/SiC and C(sub f)/SiC CMCs allows the design of lighter-weight, more fuel efficient aircraft engines and also more advanced spacecraft airframe thermal protection systems. However, CMCs have to be protected with advanced environmental barrier coatings when they are incorporated into components for the harsh environments such as in aircraft engine or spacecraft applications. In this study, high temperature oxidation kinetics of an advanced HfSiCN coating on C(sub f)/SiC CMC substrates were investigated at 1300 C, 1400 C, and 1500 C by using thermogravimetric analysis (TGA). The coating oxidation reaction parabolic rate constant and activation energy were estimated from the experimental results. The oxidation reaction studies showed that the coatings formed the most stable, predominant HfSiO4-HfO2 scales at 1400 C. A peroxidation test at 1400 C then followed by subsequent oxidation tests at various temperatures also showed more adherent scales and slower scale growth because of reduced the initial transient oxidation stage and increased HfSiO4-HfO2 content in the scales formed on the HfSiCN coatings.

environmental barrier coatings (EBCs)↗
NASA NTRS2018

Weibull-Based Stochastic Simulation of Mud-Crack Damage Formation in an Environmental Barrier Coating

The integrated Finite Element Analysis Micromechanics Analysis Code/Ceramics Analysis and Reliability Evaluation of Structures (FEAMAC/CARES) program was used to simulate the formation of mudflat-cracks from thermomechanical loading on a multi-layered Environmental Barrier Coating (EBC) system deposited on a ceramic substrate. FEAMAC/CARES combines MAC/GMC (Micromechanics Analysis Code/Generalized Method of Cells) multiscale composite micromechanics code with CARES/Life probabilistic multiaxial failure criteria code and Abaqusfinite element analysis. In this work, step function elastic modulus reduction of randomly damaged finite elements was used to represent discrete cracking events. The use of many small-sized low-aspect-ratio finite elements enabled the depiction of crack boundaries and formation of mudflat patterned damage. Demonstrated examples include finite element models of button-sized disk-shaped 3-D specimen, and a 2-D model of through-the-thickness cross-section. All models were subjected to a progressive cool down from 1300 degrees Centigrade to room temperature. Mudflat crack damage in the coating system resulted from the buildup of residual tensile stresses between the individual material constituents from thermal expansion mismatch. A 2-parameter Weibull distribution characterized the coating layer stochastic strength response and the effect of the Weibull modulus on the formation of damage was studied here.

Residual Tensile Stress↗
NASA NTRS2017

Development of Advanced Environmental Barrier Coatings for SiC/SiC Ceramic Matrix Composites: Path Toward 2700 F Temperature Capability and Beyond

Advanced environmental barrier coating systems for SiC-SiC Ceramic Matrix Composite (CMC) turbine and combustor hot section components are currently being developed to meet future turbine engine emission and performance goals. One of the significant coating development challenges is to achieve prime-reliant environmental barrier coating systems to meet the future 2700F EBC-CMC temperature stability and environmental durability requirements. This presentation will emphasize recent NASA environmental barrier coating system testing and down-selects, particularly the development path and properties towards 2700-3000F durability goals by using NASA hafnium-hafnia-rare earth-silicon-silicate composition EBC systems for the SiC-SiC CMC turbine component applications. Advanced hafnium-based compositions for enabling next generation EBC and CMCs capabilities towards ultra-high temperature ceramic coating systems will also be briefly mentioned.

Ceramic Matrix Composite↗
NASA NTRS2017

Environmental Barrier Coating Fracture, Fatigue and High-Heat-Flux Durability Modeling and Stochastic Progressive Damage Simulation

Advanced environmental barrier coatings will play an increasingly important role in future gas turbine engines because of their ability to protect emerging light-weight SiC/SiC ceramic matrix composite (CMC) engine components, further raising engine operating temperatures and performance. Because the environmental barrier coating systems are critical to the performance, reliability and durability of these hot-section ceramic engine components, a prime-reliant coating system along with established life design methodology are required for the hot-section ceramic component insertion into engine service. In this paper, we have first summarized some observations of high temperature, high-heat-flux environmental degradation and failure mechanisms of environmental barrier coating systems in laboratory simulated engine environment tests. In particular, the coating surface cracking morphologies and associated subsequent delamination mechanisms under the engine level high-heat-flux, combustion steam, and mechanical creep and fatigue loading conditions will be discussed. The EBC compostion and archtechture improvements based on advanced high heat flux environmental testing, and the modeling advances based on the integrated Finite Element Analysis Micromechanics Analysis Code/Ceramics Analysis and Reliability Evaluation of Structures (FEAMAC/CARES) program will also be highlighted. The stochastic progressive damage simulation successfully predicts mud flat damage pattern in EBCs on coated 3-D specimens, and a 2-D model of through-the-thickness cross-section. A 2-parameter Weibull distribution was assumed in characterizing the coating layer stochastic strength response and the formation of damage was therefore modeled. The damage initiation and coalescence into progressively smaller mudflat crack cells was demonstrated. A coating life prediction framework may be realized by examining the surface crack initiation and delamination propagation in conjunction with environmental degradation under high-heat-flux and environment load test conditions.

Mechanical creep and fatigue loading condition↗