Here, this study explored a high-entropy layered oxide (HELO), LiNi 0.2 Co 0.2 Mn 0.2 Al 0.2 Fe 0.2 O 2 , prepared by coprecipitation followed by heat treatment. Coprecipitation yielded a kinetically favored product, and the subsequent heat treatment under various temperatures and times allowed tuning the material toward more thermodynamically favored structures. Refinement of X-ray powder diffraction (XRD) revealed that after 450 °C treatment, ~12% of the Ni 2+ in the structure was located within the lithium cation layer. After heat treatment at 600, 700, and 800 °C, there was a continued decrease of Ni 2+ in the lithium cation layer to 9.3, 6.3, and 3.7%, respectively. Longer heat treatment times at 800 °C decreased the level to 2.5%. Electrochemical behavior was evaluated by cyclic voltammetry, galvanostatic cycling, rate capability testing, and electrochemical impedance spectroscopy, where increased loaded voltage, functional capacity, rate capability, and decreased impedance were observed for samples treated at higher temperatures with lower cation mixing. X-ray absorption near edge spectroscopy (XANES) data indicated that the redox activity of Ni and Co was dominant in the electrochemistry, while the participation of Mn or Fe was minimal. The level of Ni oxidation state change between charge and discharge related to the heat treatment temperature where the samples with high cation mixing showed lower capacity consistent with some Ni 3+ in the transition metal layer inaccessible for electron transfer. Longer heat treatment times at 800 °C did not continue to provide a benefit in electrochemical function even with some additional reduction in cation mixing.

25 ENERGY STORAGE↗

DOE OSTI2024

Comparative S/TEM study of superconducting Ta quantum resonators by wet and dry etching types

Superconducting resonators play a pivotal role in various quantum technology applications, such as quantum computing and high-frequency communication systems. The performance of these resonators is closely tied to the properties of the superconducting films used in their fabrication. Here, in this study, we investigated the impact of wet and dry etching on tantalum (Ta) films leveraging advanced scanning transmission electron microscopy-based characterization methods and examined the morphological, chemical, and strain changes caused by the etching processes. Consequently, we report the significant differences between the two etching methods, with dry etching resulting in straight slanted sidewalls and a thinner oxidized layer, while wet etching produced curved sidewalls and undercuts. Both methods led to the formation of a residual Ta wedge at the lower part of the sidewall, causing lattice deformation, which could adversely influence the homogeneous operations of superconducting devices. These insights enhance our understanding of how etching influences superconducting films, offering valuable guidance for optimizing resonators and related devices. Our findings mark a significant stride in advancing quantum technologies and high-frequency communication by enhancing our practical understanding of superconducting material fabrication.

36 MATERIALS SCIENCE↗