DOE OSTI2024

Microstructure, electrical resistivity, and tensile properties of neutron-irradiated Cu–Cr–Nb–Zr

High strength, high conductivity copper alloys that can resist creep at high temperatures are one of the primary candidates for efficient heat exchangers in fusion reactors. Cu–Cr–Nb–Zr (CCNZ) alloys, which were designed to improve the strength and creep life of ITER Cu–Cr–Zr (CCZ) reference alloys, have been found to have comparable electrical conductivity and tensile properties to CCZ alloys. The measured creep rupture times for these improved alloys is about ten times higher than the ITER reference alloys at 90–125 MPa at 500 °C. However, the effects of neutron irradiation on these alloys, and the ensuing material properties, have not been studied; thus, their utility in a fusion reactor environment is not well understood. This study characterizes the room temperature mechanical and electrical properties of a neutron-irradiated CCNZ alloy and compares them to a neutron-irradiated ITER reference heat sink CCZ alloy. Tensile specimens were neutron irradiated in the High Flux Isotope Reactor (HFIR) to 5 dpa between 250 °C and 325 °C. Post-irradiation characterization included electrical resistivity measurements, hardness, and tensile tests. Microstructural evaluation used scanning electron microscopy, energy dispersive x-ray spectroscopy, and atom probe tomography to characterize the irradiation-produced changes in the microstructure and investigate the mechanistic processes leading to post-irradiation properties. Transmutation calculations were validated with composition measurements from atom probe data and used to calculate contributions to the increased electrical resistivity measured after irradiation. Comparisons with CCZ alloys in the same irradiation heat found that the post-irradiated CCNZ and CCZ alloys had comparable electrical resistivity. Although CCNZ alloys suffered more irradiation hardening than CCZ, the overall tensile behavior deviated very little from non-irradiated values in the temperature range studied.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Understanding Formation of Irradiation-Induced Defects through 4D-STEM, Electron Tomography, and WBDF-STEM

A major challenge in advancing nuclear materials for next-generation fission and proposed fusion reactors is to comprehensively understand the formation of irradiation-induced defects. Here it is essential to correlate the evolution of irradiation-induced defects and the degradation of mechanical properties, as they collectively dictate the material's lifespan and ensure nuclear safety. Scanning transmission electron microscopy (STEM) based techniques have emerged as indispensable tools for irradiation-induced defect characterization, offering high spatial resolution imaging and chemical analysis, such as electron energy loss spectroscopy (EELS) and energy dispersive X-ray spectroscopy (EDXS). These techniques have been effectively used to obtain an atomic-scale view of the defect structure. Recent advances in electron microscopy, particularly in 4D-STEM, offer detailed insight into microstructural evolution by capturing full 2D diffraction patterns at every pixel position. Using high-speed direct electron detectors, this technology generates a four-dimensional dataset, overcoming the limitations of traditional STEM imaging.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Application of Weak-Beam Dark-Field STEM for Dislocation Loop Analysis

Nanoscale dislocation loops formed by irradiation can significantly contribute to both irradiation hardening and embrittlement of materials when subjected to extreme nuclear reactor environments. Here, this study explores the application of weak-beam dark-field (WBDF) scanning transmission electron microscopy (STEM) methods for quantitative irradiation-induced defect analysis in crystalline materials, with a specific focus on dislocation loop imaging and analysis. A high-purity Fe-5 wt% Cr model alloy was irradiated with 8 MeV Fe 2+ ions at 450°C to a fluence of 8.8 × 10 19 m -2 , inducing dislocation loops for analysis. While transmission electron microscopy (TEM) has traditionally been the primary tool for dislocation imaging, recent advancements in STEM technology have reignited interest in using STEM for defect imaging. This study introduces and compares three WBDF STEM methods, demonstrating their effectiveness in suppressing background contrasts, isolating defect information for dislocation loop type classification, providing finer dislocation line images for small loop analysis, and presenting inside–outside contrast for identifying loop nature. Experimental findings indicate that WBDF STEM methods surpass traditional TEM approaches, yielding clearer and more detailed images of dislocation loops. The study concludes by discussing the potential applications of WBDF STEM techniques in defect analysis, emphasizing their adaptability across various material systems beyond nuclear materials.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Comparison of hardening and microstructures of ferritic/martensitic steels irradiated with fast neutrons and dual ions

Ferritic/martensitic steels T91 and HT9 were irradiated with neutrons (BOR-60 reactor) and dual ions (9 MeV Fe 3+ and 3.42 MeV energy degraded He 2+ ) from 369 to 520 °C and damage levels of 16.6 to 72 dpa to quantify the possibility of using ion irradiation to simulate neutron irradiation in terms of microstructures and mechanical properties. Nanoindentation testing was performed to obtain the bulk equivalent hardness of the dual-ion irradiated samples. For the neutron irradiated samples, both nanoindentation and Vickers hardness testing were conducted. Transmission Electron Microscopy (TEM) characterizations of the cavities, dislocation loops and precipitates were conducted to account for the strengthening contribution of each microstructure element. The good agreement between the microstructure-predicted (dispersed barrier hardening) and measured strength of the irradiated specimens demonstrated the accuracy of the strengthening model and the nanoindentation tests. Furthermore, the comparison of mechanical property and microstructure changes in ion and neutron irradiated structural materials indicated that ion irradiation replicated many neutron irradiation features. However, a single 70 °C temperature shift is insufficient to match all complex microstructures of neutron vs. ion irradiation over the irradiation temperature range of 369–520 °C.

36 MATERIALS SCIENCE↗