NASA NTRS2011

Degradation of Multi-Layer Insulation (MLI) Retrieved from the Hubble Space Telescope

Multi-Layer Insulation (MLI) returned during Servicing Mission 4 are still being analyzed. Analysis has revealed degradation of optical, thermal, and mechanical properties, increased crystallinity, and reduction in fluorine/carbon ratio of aluminized-Teflon fluorinated ethylene propylene (Al-FEP) FEP. These material properties can be affected by high temperatures on orbit, increased radiation exposure, and in some cases contamination from materials in close proximity to the insulation on orbit. Preliminary results support conclusions of previous studies: areas of Al-FEP that received higher levels of solar exposure show more degradation (high temperatures and radiation combined).

Mohammed, Jelila S.↗

NASA NTRS2010

MISSE 2 PEACE Polymers Experiment Atomic Oxygen Erosion Yield Error Analysis

Atomic oxygen erosion of polymers in low Earth orbit (LEO) poses a serious threat to spacecraft performance and durability. To address this, 40 different polymer samples and a sample of pyrolytic graphite, collectively called the PEACE (Polymer Erosion and Contamination Experiment) Polymers, were exposed to the LEO space environment on the exterior of the International Space Station (ISS) for nearly 4 years as part of the Materials International Space Station Experiment 1 & 2 (MISSE 1 & 2). The purpose of the PEACE Polymers experiment was to obtain accurate mass loss measurements in space to combine with ground measurements in order to accurately calculate the atomic oxygen erosion yields of a wide variety of polymeric materials exposed to the LEO space environment for a long period of time. Error calculations were performed in order to determine the accuracy of the mass measurements and therefore of the erosion yield values. The standard deviation, or error, of each factor was incorporated into the fractional uncertainty of the erosion yield for each of three different situations, depending on the post-flight weighing procedure. The resulting error calculations showed the erosion yield values to be very accurate, with an average error of 3.30 percent.

McCarthy, Catherine E.↗

NASA NTRS2008

Lessons Learned From Atomic Oxygen Interaction With Spacecraft Materials in Low Earth Orbit

There have been five Materials International Space Station Experiment (MISSE) passive experiment carriers (PECs) (MISSE 1-5) to date that have been launched, exposed in space on the exterior of International Space Station (ISS) and then returned to Earth for analysis. An additional four MISSE PECs (MISSE 6A, 6B, 7A, and 7B) are in various stages of completion. The PECs are two-sided suitcase to size sample carriers that are intended to provide information on the effects of the low Earth orbital environment on a wide variety of materials and components. As a result of post retrieval analyses of the retrieved MISSE 2 experiments and numerous prior space experiments, there have been valuable lessons learned and needs identified that are worthy of being documented so that planning, design, and analysis of future space environment experiments can benefit from the experience in order to maximize the knowledge gained. Some of the lessons learned involve the techniques, concepts, and issues associated with measuring atomic oxygen erosion yields. These are presented along with several issues to be considered when designing experiments, such as the uncertainty in mission duration, scattering and contamination effects on results, and the accuracy of measuring atomic oxygen erosion.

Banks, Bruce A.↗

NASA NTRS2007

Comparison of the Atomic Oxygen Erosion Depth and Cone Height of Various Materials at Hyperthermal Energy

Atomic oxygen readily reacts with most spacecraft polymer materials exposed to the low Earth orbital (LEO) environment. If the atomic oxygen arrival comes from a fixed angle of impact, the resulting erosion will foster the development of a change in surface morphology as material thickness decreases. Hydrocarbon and halopolymer materials, as well as graphite, are easily oxidized and textured by directed atomic oxygen in LEO at energies of approx.4.5 eV. What has been curious is that the ratio of cone height to erosion depth is quite different for different materials. The formation of cones under fixed direction atomic oxygen attack may contribute to a reduction in material tensile strength in excess of that which would occur if the cone height to erosion depth ratio was very low because of greater opportunities for crack initiation. In an effort to understand how material composition affects the ratio of cone height to erosion depth, an experimental investigation was conducted on 18 different materials exposed to a hyperthermal energy directed atomic oxygen source (approx.70 eV). The materials were first salt-sprayed to provide microscopic local areas that would be protected from atomic oxygen. This allowed erosion depth measurements to be made by scanning microscopy inspection. The polymers were then exposed to atomic oxygen produced by an end Hall ion source that was operated on pure oxygen. Samples were exposed to an atomic oxygen effective fluence of 1.0x10(exp 20) atoms/sq cm based on Kapton H polyimide erosion. The average erosion depth and average cone height were determined using field emission scanning electron microscopy (FESEM). The experimental ratio of average cone height to erosion depth is compared to polymer composition and other properties.

Waters, Deborah L.↗

NASA NTRS2006

MISSE PEACE Polymers Atomic Oxygen Erosion Results

Forty-one different polymer samples, collectively called the Polymer Erosion and Contamination Experiment (PEACE) Polymers, have been exposed to the low Earth orbit (LEO) environment on the exterior of the International Space Station (ISS) for nearly 4 years as part of Materials International Space Station Experiment 2 (MISSE 2). The objective of the PEACE Polymers experiment was to determine the atomic oxygen erosion yield of a wide variety of polymeric materials after long term exposure to the space environment. The polymers range from those commonly used for spacecraft applications, such as Teflon (DuPont) FEP, to more recently developed polymers, such as high temperature polyimide PMR (polymerization of monomer reactants). Additional polymers were included to explore erosion yield dependence upon chemical composition. The MISSE PEACE Polymers experiment was flown in MISSE Passive Experiment Carrier 2 (PEC 2), tray 1, on the exterior of the ISS Quest Airlock and was exposed to atomic oxygen along with solar and charged particle radiation. MISSE 2 was successfully retrieved during a space walk on July 30, 2005, during Discovery s STS-114 Return to Flight mission. Details on the specific polymers flown, flight sample fabrication, pre-flight and post-flight characterization techniques, and atomic oxygen fluence calculations are discussed along with a summary of the atomic oxygen erosion yield results. The MISSE 2 PEACE Polymers experiment is unique because it has the widest variety of polymers flown in LEO for a long duration and provides extremely valuable erosion yield data for spacecraft design purposes.

deGroh, Kim, K.↗

NASA NTRS2006

Solar Effects on Tensile and Optical Properties of Hubble Space Telescope Silver-Teflon(Registered Trademark) Insulation

A section of the retrieved Hubble Space Telescope (HST) solar array drive arm (SADA) multilayer insulation (MLI), which experienced 8.25 years of space exposure, was analyzed for environmental durability of the top layer of silver-Teflon (DuPont) fluorinated ethylene propylene (Ag-FEP). Because the SADA MLI had solar and anti-solar facing surfaces and was exposed to the space environment for a long duration, it provided a unique opportunity to study solar effects on the environmental degradation of Ag-FEP, a commonly used spacecraft thermal control material. Data obtained included tensile properties, solar absorptance, surface morphology and chemistry. The solar facing surface was found to be extremely embrittled and contained numerous through-thickness cracks. Tensile testing indicated that the solar facing surface lost 60% of its mechanical strength and 90% of its elasticity while the anti-solar facing surface had ductility similar to pristine FEP. The solar absorptance of both the solar facing surface (0.155 plus or minus 0.032) and the anti-solar facing surface (0.208 plus or minus 0.012) were found to be greater than pristine Ag-FEP (0.074). Solar facing and anti-solar facing surfaces were microscopically textured, and locations of isolated contamination were present on the anti-solar surface resulting in increased localized texturing. Yet, the overall texture was significantly more pronounced on the solar facing surface indicating a synergistic effect of combined solar exposure and increased heating with atomic oxygen erosion. The results indicate a very strong dependence of degradation, particularly embrittlement, upon solar exposure with orbital thermal cycling having a significant effect.

deGroh, Kim, K.↗

NASA NTRS2006

Comparison of Atomic Oxygen Erosion Yields of Materials at Various Energy and Impact Angles

The atomic oxygen erosion yields of various materials, measured in volume of material oxidized per incident atomic oxygen atom, are compared to the commonly accepted standard of Kapton H (DuPont) polyimide. The ratios of the erosion yield of Kapton H to the erosion yield of various materials are not consistent at different atomic oxygen energies. Although it is most convenient to use isotropic thermal energy RF plasma ashers to assess atomic oxygen durability, the results can be misleading because the relative erosion rates at thermal energies are not necessarily the same as low Earth orbital (LEO) energies of approx.4.5 eV. An experimental investigation of the relative atomic oxygen erosion yields of a wide variety of polymers and carbon was conducted using isotropic thermal energy (approx.0.1 eV) and hyperthermal energy (approx.70 eV) atomic oxygen using an RF plasma asher and an end Hall ion source. For hyperthermal energies, the atomic oxygen erosion yields relative to normal incident Kapton H were compared for sweeping atomic oxygen arrival with that of normal incidence arrival. The results of isotropic thermal energy, normal incident, and sweeping incident atomic oxygen are also compared with measured or projected LEO values.

Banks, Bruce A.↗

NASA NTRS2002

Physical and Thermal Properties Evaluated of Teflon FEP Retrieved From the Hubble Space Telescope During Three Servicing Missions

Mechanical properties of aluminized Teflon fluorinated ethylene propylene (FEP) thermal control materials on the Hubble Space Telescope (HST) exposed to low Earth orbit for up to 9.7 years have significantly degraded, with extensive cracking occurring on orbit. The NASA Glenn Research Center and the NASA Goddard Space Flight Center have collaborated on analyzing the physical and thermal properties of aluminized FEP (FEP-Al, DuPont) materials retrieved in December 1999 during HST's third servicing mission (SM3A). Comparisons have been made to properties of FEP-Al retrieved during the first and second HST servicing missions, SM1 and SM2, in order to determine degradation processes for FEP on HST.

Dever, Joyce A.↗