Prediction of strain, inter-layer interaction and critical current in CORC ® wires under axial strain by T-A modeling
Superconducting conductors on round core (CORC ® ) cables and wires can meet the needs of large high-field magnets, such as particle accelerators and compact nuclear fusion machines, due to their simple cabling process, high current-carrying capacity and reliable operation under high mechanical stresses. Many high-field magnets require CORC ® cables to carry a current of thousands of amperes in a background magnetic field exceeding 20 T. As a result, the large electromagnetic forces will deform the cable in the axial direction due to hoop stress and in the transverse direction by compressive stress. Therefore, it is essential to determine the irreversible deformation limit of the CORC ® cable under axial tensile load and optimize the cabling parameters to potentially extend this limit. Analytical and numerical methods are developed to assess the performance degradation of CORC ® wires under axial tensile load. The strain level, interlayer contact pressure and friction and their impact on the critical current are calculated by combining the mechanical response and the T-A method. Analyzing the results shows that the winding angle of the tape and the Poisson’s ratio of the inner core are key factors affecting the irreversible tensile strain limit of CORC ® wires. The smaller the winding angle and the higher the Poisson’s ratio of the inner core, the higher the irreversible tensile strain limit. For multi-layer CORC ® wires, the initial contact pressure caused by the cabling process must also be considered. The inter-layer interaction is coupled with the tape strain of each layer. The results of this research can serve as a basis for optimizing and designing CORC ® wires with extended irreversible strain limits.
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
A turnkey gaseous helium-cooled superconducting CORC ® dc power cable with integrated current leads
Abstract High-temperature superconducting (HTS) direct current (dc) power cable systems, capable of delivering power exceeding 10 MW while being cooled with cryogenic helium gas, have been developed for applications on naval electric ships, electric aircraft and in data centers. Current injection from room temperature into the superconducting power cable causes by far the greatest heat load to the cryogenic system. Efficient current leads with integrated helium gas heat exchangers were developed to inject a current exceeding 1 kA from room temperature into a superconducting Conductor on Round Core (CORC ® ) power cable, without the need for liquid nitrogen pre-cooling. A 2 m long single-pole CORC ® power cable system that included current leads was cooled using a Stirling cryocooler with a closed-loop helium gas circulation system. The turnkey power cable system allowed cool down from room temperature to its operating temperature of 60 K–70 K within 5 h, after which continuous operation at 1.2 kA was demonstrated. The successful development and demonstration of a CORC ® power cable with current leads containing integrated helium gas heat exchangers enables widespread implementation of HTS MW-class, high current density superconducting dc power cables in many applications with constrained space that require a power dense solution.
Physics↗
High-temperature superconducting CORC ® wires with record-breaking axial tensile strain tolerance present a breakthrough for high-field magnets
Cuprate high-temperature superconductors (HTS), such as RE-Ba 2 Cu 3 O 7–δ (REBCO, RE = rare earth), (Bi,Pb) 2 Sr 2 Ca 2 Cu 3 O 10–x and Bi 2 Sr 2 CaCu 2 O 8–x , have enabled the development of high-field superconducting magnets capable of generating magnetic fields far exceeding 20 T. The brittle nature of HTS requires elaborate means to protect them against the high stresses and strains associated with high-field magnet operation, and so far, has prevented reliable high-field HTS magnets from becoming a reality. Here we report a more than tenfold increase in the irreversible strain limit under axial tension (epsilonirr) to over 7% in optimized high-current conductor on round core (CORC®) conductors, compared to the REBCO tapes from which the CORC® conductor is wound. Minimizing the tape winding pitch of the helical wind mechanically decouples the brittle REBCO film from the overall conductor. The REBCO tapes behave as springs, limiting the rate at which applied strain is transferred to the ceramic film. In addition, high-strength alloy cores allow the critical stress (ϵ crit ) under axial tension at which initial degradation of CORC® conductors occurs to exceed 600 MPa, making them one of the strongest superconductors available. Mechanically decoupling the ceramic REBCO films from the overall CORC® conductor allows effective protection against the high operating stresses in high-field magnets. Furthermore, this breakthrough presents a monumental shift for HTS magnet technology, bringing reliable high-field superconducting magnets for compact fusion machines, the next generation of particle accelerators, and 40–60 T research solenoids within reach.
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
Quench detection using Hall sensors in high-temperature superconducting CORC ® -based cable-in-conduit-conductors for fusion applications
Advanced magnet systems for fusion applications would greatly benefit from the use of high-temperature superconductors (HTS). These materials allow fusion magnets to operate at higher magnetic fields, allowing for more compact fusion machines, and allow for operation at elevated temperatures, enabling demountable coils that provide access for maintenance of the fusion reactor. Quench detection remains a major challenge in the protection of HTS magnets that are vulnerable to localized conductor burnout due to their low quench propagation velocities. One of the methods explored is the use of Hall sensors that are incorporated in or near the magnet terminations that can detect local field variations that occur as a result of current redistribution within the conductor to bypass a hotspot within the magnet winding. This method is potentially well suited for Cable in Conduit Conductors, such as those made from Conductor on Round Core (CORC) cables, in which sub-cables containing HTS tapes are connected to the terminations at a low resistance. Here, to demonstrate the technique, a CORC ® triplet consisting of three sub-cables, rated for 4 kA operation at 77 K, was manufactured and Hall sensors were used to measure local field variations next to the terminations due to current redistribution between the cables. The Hall response was compared to voltages that developed over the cables and terminations as a local hotspot was applied to different cables in the triplet. It was found that the Hall sensors were faster and more sensitive than voltage contact measurements and were able to reliably detect current redistribution of only a few amperes caused by a hotspot, well before the triplet exceeded its critical current. The method also allowed the detection of heater-induced hotspots during high ramp rates of 2 kA s<:sup>–1 relevant for fusion applications. Hall sensors have a distinct benefit of being less sensitive to inductive pickup of AC interference compared to voltage contact measurements that make quench detection through voltage measurements in magnets especially challenging. The method can also be used for diagnostic measurements of current redistribution caused by other sources such as inhomogeneous current injection from faulty joints, or localized conductor damage. The Hall sensors are likely capable of detecting the onset of a quench that may occur a far distance away from the sensor location, presenting a breakthrough in HTS quench detection that potentially removes one of the remaining barriers to reliable operation of large HTS magnet systems.
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗