Analysis of stress-rupture data from S-glass composites.

Abstract

Both composite and free strands have been tested to study matrix effectiveness. Glass from different lots were used, and processing parameters were varied to demonstrate the effects of material variability. The statistical patterns that emerge from these experiments show that lifetime distributions are characteristically skewed. As a class, the lifetime distributions are well approximated by the reduced form of the Weibull distribution. The strength retention data display little early degradation. The retained-strength distributions can also be classed as Weibull distributions. A statistical model applied to the data gives predictions of progressive failure, strength retention path, and expected life for two basic types of internal fracture processes.