Fabrication and life testing of thermionic converters

Abstract

An unfueled converter containing a chloride-fluoride duplex tungsten emitter of 4.78 eV vacuum work function was tested for 46,647 hours at an emitter temperature of 1973 K and an electrode power output of about 8 watts/sq cm. The test demonstrated the superior and stable performance of the (110) oriented tungsten emitter at high temperatures. Three 90 UC-10 ZrC(C/U = 1.04, tungsten additive = 4 wt %) fueled converters were fabricated and tested at an emitter temperature of 1873 K. Converter containing chloride-arc-cast duplex tungsten cladding showed temperature thermionic performance and slower rate of performance drop than converter containing chloride-fluoride duplex tungsten cladding. This is believed to be due to the superior fuel component diffusion resistance of the arc-cast tungsten substrate used in the fuel cladding. It was shown that a converter containing a carbide fueled chloride-arc-cast duplex tungsten emitter with an initial electrode power output of 6.80 watts/sq cm could still deliver an electrode power output of 6.16 watts/sq cm after 18,632 hours of operation at an emitter temperature of 1873 K.