High temperature superconductor NB3Ga

Abstract

The discovery of superconductivity at 20.3 K in the Nb-Ga system by applying chemical vapor deposition (CVD) techniques to the materials preparation problem is reported. Films on ceramic substrates have been grown with superconducting onsets of up to 20.3 K. Critical fields at 4.2 K in excess of 300 kG and alpha's of 1100,000 T-A/sq cm have been obtained. The results confirm that the outstanding properties of Nb-Ga are due to an equilibrium configuration of the system, namely, the stoichiometric A-15 compound Nb3Ga, which is stable at relatively low temperatures. Practical materials preparation problems center on the codeposition of an adjacent Nb5Ga3 phase and the requirement that the deposition temperature be low. Some ternary alloys were also prepared, with part of the Ga replaced by Sn, Sb, Al, or Ge.