Containerless processing of single crystals in low-G environment

Abstract

Experiments on containerless crystal growth from the melt were conducted during Skylab missions SL3 and SL4 (Skylab Experiment M-560). Six samples of InSb were processed, one of them heavily doped with selenium. The concept of the experiment is discussed and related to general crystal growth methods and their merits as techniques for containerless processing in space. The morphology of the crystals obtained is explained in terms of volume changes associated with solidification and wetting conditions during solidification. All samples exhibit extremely well developed growth facets. Analysis by X-ray topographical methods and chemical etching shows that the crystals are of high structural perfection. Average dislocation density as revealed by etching is of the order of 100 per sq cm; no dislocation clusters could be observed in the space-grown samples. A sequence of striations that is observed in the first half of the selenium-doped sample is explained as being caused by periodic surface breakdown.