Exploratory study on microanalysis of thin films by backscattering techniques

Abstract

Solid phase epitaxial growth of Si layers was studied by backscattering spectrometry for controllable electrical characteristics. Samples were fabricated by vacuum deposition on a thin layer of Sb before deposition of the amorphous Si layer. Analysis of the resulting SPEG layer showed that Sb was present in the SPEG layer of Si. The characteristic of the SPEG layer against the Si substrate was rectifying. A scanning microprobe picture of a cleaved sample established the presence of a depletion region more than 1 micron below the surface. Hall effect data indicated that the SPEG layer was n-type, with average free carrier concentration of about 10 to the 19th power cm/3 and average electron mobility of about 40 sq cm/Vs. SPEG with Pd silicide or Ni silicide transport layers showed fast initial transient growth regimes with slower growth in the steady state regimes.