Development of a high efficiency thin silicon solar cell

Abstract

One hundred thin (120 microns to 260 microns) silicon-aluminum solar cells were fabricated and tested. Silicon slices were prepared, into which an aluminum alloy was evaporated over a range of temperatures and times. Antireflection coatings of tantalum oxide were applied to the cells. Reflectance of the silicon-aluminum interfaces was correlated to alloy temperature (graphs are shown). Optical measurements of the rear surface-internal reflectance of the cells were performed using a Beckman spectrophotometer. An improved gridline pattern was evaluated and stability tests (thermal cycling tests) were performed. Results show that: (1) a high-index, high-transmittance antireflection coating was obtained; (2) the improved metallization of the cells gave a 60 percent rear surface-internal reflectance, and the cells displayed excellent fill factors and blue response of the spectrum; (3) an improved gridline pattern (5 micron linewidths compared to 13 micron linewidths) resulted in a 1.3 percent improvement in short circuit currents; and (4) the stability tests showed no change in cell properties.