Further development of high temperature-resistant graphite fiber coupling agents

Abstract

Potential coupling agents for graphite fibers were screened by their effect on the weight losses of Thornel 300, HMS, and HTS fibers at 588K for 200 and 400 hours. Unidirectional laminates were made from HMS and HTS fibers, untreated, and treated with each of the seven coupling agents. The matrix of all laminates was PMR polyimide (PMR-PR). On the basis of the best overall retention of elevated temperature interlaminar shear strength after 200 hours at 588K, composite weight after 200 hours at 588K, and fiber weight after 400 hours at 588K, ventromer T-1 applied from aqueous solution and pyrolyzed PPQ were selected for further evaluation as coupling agents for HTS fiber while ventromer T-2 and pyrolyzed PPQ were selected as coupling agents for HMS fiber. It was shown that pyrolyzed PPQ as a coupling agent improves the oxidative stability of HTS/PMR-PI composites.