Alloy softening in binary iron solid solutions

Abstract

An experimental study was conducted to determine whether alloy softening in Fe alloys is dependent on electron concentration and to provide a direct comparison of alloy softening and hardening in several binary Fe alloy systems having the same processing history. Alloy additions to Fe included the elements in the Periods 4-6 and the Groups IV-VIII with the exception of technetium. A total of 19 alloy systems was investigated, and hardness testing was the primary means of evaluation. Testing was carried out at four temperatures over a homologous temperature range of 0.043-0.227 times the absolute melting temperature of unalloyed Fe. Major conclusions are that the atomic radius ratio of solute-to-Fe is the key factor in controlling low-temperature hardness of the binary Fe alloys and that alloy softening rates at 77 K and alloy hardening rates at 411 K are correlated with this atomic radius ratio for 15 of the binary alloy systems. Mechanisms of alloy softening and hardening are proposed.