Fatigue damage of notched boron/epoxy laminates under constant amplitude loading

Abstract

Fatigue damage in (0, + or - 45) and (0, + or - 45,90) boron/epoxy laminates was studied with X-ray radiography and scanning electron microscopy. In addition, limited tests for residual strength and stiffness were performed. The results of this study suggest that in boron/epoxy laminates the 45-degree plies play a key role in the fatigue process of boron/epoxy laminates that contain them. The fatigue process in the + or - 45-degree plies starts as intralaminar matrix cracks.