Processing eutectics in space

Abstract

The examination of the Ni-Mo-Al system is discussed. Experiments were performed to examine the role of thermal gradient magnitude at the solidifying interface on the geometrical regularity of the microstructure. The difficulty in measuring the thermal gradient in the melt using superheat temperatures as high as 1800 C resulted in the examination of three liquid temperature gradient ranges. Examination of the microstructure from directionally solidified ingots using transverse sections indicated that the highest gradient runs produced microstructure of no greater regularity than runs made at lower gradients. For the Ni-Al-Mo monovariant eutectic system, the magnitude of the thermal gradient at the solidifying interface is not a controlling parameter with respect to the geometrical regularity of the microstructure, provided it is sufficient to satisfy the gradient/rate ratio needed to produce a planar interface growth.