Spar I liquid mixing experiment

Abstract

The Liquid Mixing Experiment had as its objective the observation of effects of residual acceleration on a confined fluid system. The fluid system was chosen to be similar geometrically and in fluid properties to a range of materials science experiments. Samples were constructed as cylinders 2.2 cm long by 0.6 cm diameter. Half of each cylinder was composed of pure indium, and the other half of each was an alloy of 80 wt% indium and 25 wt% lead. The samples were enclosed in aluminum cartridges and placed in heaters mounted in three mutually perpendicular directions. The experimental procedure consisted of melting the samples when the low-g phase of the payload trajectory was attained, holding the samples in a molten state for approximately 200 seconds, and then quenching to resolidification before leaving low-g. Two of the samples exhibited very little fluid motion. The third sample, which was oriented nearly parallel to a payload radius, showed a great deal of flow.