Fracture surface characteristics of off-axis composites

Abstract

The fracture surface characteristics of off-axis high-modulus graphite-fiber/epoxy composite specimens were studied using a scanning electron microscope (SEM). The specimens were subjected to tensile loading at various angles (0-90 deg) to the fiber direction. SEM photomicrographs of the fractured surfaces revealed three different load angle regions with distinct fracture characteristics. Based on these revelations, criteria were established which can be used to characterize fracture surfaces with respect to a predominant 'single-stress' fracture mode.