Low density bismaleimide-carbon microballoon composites

Abstract

A process is described for the preparation of composite laminate.structures of glass cloth preimpregnated with polybismaleimide resin and adhered to a polybismaleimide glass or aromatic polyamide paper honeycomb cell structure that is filled or partially filled with a syntactic foam consisting of a mixture of bismaleimide resin and carbon microballoons. The carbon microballoons are prepared by pyrolyzing phenolic microballoons and subsequently bonded using a 2% bismaleimide solution. The laminate structures are cured for two hours at 477 deg K and are adhered to the honeycomb bismaleimide adhesive using a pressure of 700 KN/sq m pressure at 450 deg K. The laminate composite is then post-cured for two hours at 527 deg K to produce a composite laminate having a density in the range from about 95 kilograms per cubic meter to 130 kilograms per cubic meter.