Development of an Improved High Efficiency Thin Silicon Solar Cell

Abstract

Breakage and front contact failure in high efficiency, textured ultrathin cells was reduced as a consequence of the introduction of process modifications. In a small production run, over one hundred ultrathin cells, having an average AMO efficiency of 13%, were fabricated from 10-25 ohm cm silicon. An in-house aluminum paste for back surface field formation was developed that resulted in cell efficiencies equivalent to those from commercial pastes. The quality of the back surface field was found to be dependent on the orientation of the silicon slice during alloying.