Growth parameters for aligned microstructures in directionally solidified aluminum-bismuth monotectic

Abstract

Microstructures are shown for directionally solidified Al-3.4 wt pct Bi alloys with 0.2 wt pct Fe and 0.6 wt pct Fe additions. The third element causes the LI/SI + LII growth interface to become cellular. The bismuth forms at the cell nodes, appearing either as uniformly spaced arrays of spheres in the case of 0.2 wt pct Fe, or as an irregular network in the case of 0.6 wt pct Fe. Changes in the growth conditions which are known to control cellular structure are seen to have a similar effect on the bismuth spacing, with the cross sectional spacing varying as the inverse of G (Temperature gradient) x R(Growth rate).