Development of Mullite Substrates and Containers

Abstract

The mullite-molten silicon interaction was evaluated through fabrication of a series of bodies made with variations in density, alumina-silica ratio, and glass-crystalline ratio. The materials were tested in a sessile drop technique. None of the variations stood up to extended exposure to molten silicon sufficiently to be recommended as a container material. However, directional solidification experiments suggest that, under proper conditions, contamination of the silicon by mullite containers can be minimized. To improve an already good thermal expansion match between mullite and silicon, compositional variations were studied. Altering of the alumina-silica ratio was determined to give a continuously varying thermal expansion. A standard mullite composition was selected and substrates 40 x 4 x .040 inches were fabricated. Slotted substrates of various configurations and various compositions were also fabricated.