IUS materials outgassing condensation effects on sensitive spacecraft surfaces

C. R. Mullen·C. G. Shaw·E. R. Crutcher
View original source ↗Export metadata ↓

Abstract

Four materials used on the inertial upper state (IUS) were subjected to vacuum conditions and heated to near-operational temperatures (93 to 316 C), releasing volatile materials. A fraction of the volatile materials were collected on 25 C solar cells, optical solar reflectors (OSR's) or aluminized Mylar. The contaminated surfaces were exposed to 26 equivalent sun hours of simulated solar ultraviolet (UV) radiation. Measurements of contamination deposit mass, structure, reflectance and effects on solar cell power output were made before and after UV irradiation. Standard total mass loss - volatile condensible materials (TML - VCM) tests were also performed. A 2500 A thick contaminant layer produced by EPDM rubber motor-case insulation outgassing increased the solar absorptance of the OSR's from 0.07 to 0.14, and to 0.18 after UV exposure. An 83,000 A layer caused an increase from 0.07 to 0.21, and then the 0.46 after UV exposure. The Kevlar-epoxy motor-case material outgassing condensation raised the absorptance from 0.07 to 0.13, but UV had no effect. Outgassing from multilayer insulation and carbon-carbon nozzle materials did not affect the solar absorptance of the OSR's.

Keep this discovery

BibTeXRIS

C. R. Mullen, C. G. Shaw, E. R. Crutcher. 1982-01-01. IUS materials outgassing condensation effects on sensitive spacecraft surfaces. https://ntrs.nasa.gov/citations/19820017435

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related discoveries

NASA NTRS2026

Gateway Element and Payload Materials Outgassing Analyses: HALO, HERMES, and ERSA

Gateway was intended to be humanity’s first space station around the Moon, but its development has been paused as the National Aeronautics and Space Administration (NASA) shifts focus to achieving the United States’ National Space Policy goals. Instead of an orbiting lunar outpost, NASA will now pursue the development of a lunar surface base to support a sustained human presence on the Moon. Before the program’s pause, Gateway’s Induced Environments team worked to ensure payloads and elements (i.e., modules) complied with induced environment requirements. Methods developed and insights gained from this work will have applicability to NASA’s Moon Base and the potential repurposing of Gateway elements and payloads, as well as to induced environments modeling for future space stations. The Gateway program’s induced environment included molecular contamination, electric thruster plume sputter and redeposition, and lunar dust transfer from the Human Landing System (HLS). Primary sources of external molecular contamination included materials outgassing, chemical thruster plume contamination, and vacuum venting. The focus of this paper will be on element- and payload-level materials outgassing analyses performed for Gateway Configuration 1, extending the previously-developed framework for Gateway system-level external molecular contamination modeling. Gateway Configuration 1 consisted of the Power and Propulsion Element (PPE) and the Habitation and Logistics Outpost (HALO). It also included payloads like the European Radiation Sensor Array (ERSA) attached to PPE and the Heliophysics Environmental and Radiation Measurement Experiment Suite (HERMES) attached to HALO. The element- and payload-level analyses to be introduced in this paper for HALO, HERMES, and ERSA enabled high-fidelity descriptions of Gateway’s external molecular contamination environment. Approaches to geometric modeling, meshing, outgassing rate assignment, molecular transport modeling, and analysis methodology will be presented. Element and payload contaminant deposition onto sensitive Gateway receiver surfaces will be summarized and results compared to induced environment requirements. While these results incorporate refinements made over the course of the program, they were not intended to be final. Therefore, modeling assumptions and inputs, potential improvements, and lessons-learned will be documented to inform future work on Moon Base, repurposed elements and payloads, and other space stations.

Gateway↗
NASA NTRS1990

Satellite Material Contaminant Optical Properties

The Air Force Wright Research and Development Center and the Arnold Engineering Development Center are continuing a program for measuring optical effects of satellite material outgassing products on cryo-optic surfaces. Presented here are infrared (4000 to 700 cm -1 ) transmittance data for contaminant films condensed on a 77 K geranium window. From the transmittance data, the contaminant film refractive and absorptive indices (n, k) were derived using an analytical thin-film interference model with a nonlinear least-squares algorithm. To date 19 materials have been studied with the optical contents determined for 13 of those. The materials include adhesives, paints, composites, films, and lubricants. This program is continuing and properties for other materials will be available in the future.

B E Wood↗
NASA NTRS2026

Outgassing Characterization of Common Trash Items for Disposal By Nanoracks Airlock on the International Space Station

The arrival of the Nanoracks Airlock to the International Space Station (ISS) has provided the ISS program the capability to dispose of common trash items. The concept of operations involved the crew bagging up those items into a trash bag and then utilizing the robotic arm and the airlock to jettison the trash bag. Because of the unknown thermal vacuum stability of some of the items, a molecular contamination concern was raised by the ISS program as the trash is exposed to vacuum upon the evacuation of air from the airlock and the robotic arm moving the airlock to its jettison location. In order to characterize the representative outgassing rates for ISS trash, thermal vacuum testing was performed at White Sands Test Facility. Trash was sorted into a “lower” outgassing bag and a “mixed” bag. The “mixed” trash bag contained more items that were suspected to be not vacuum stable. Load cells were chosen as the primary means for measuring mass loss. A sharp decay in the outgassing rate was observed in the first 30 minutes followed by a slower decay. As expected, the “mixed” bag lost more mass. While Quartz Crystal Microbalances (QCMs) are often utilized to measure long term outgassing rates and the sticking coefficients of contaminants at different operating temperatures for vacuum stable materials, these measurements proved difficult due to the amount and the inclusion of materials with suspect thermal vacuum stability. Because of high rates of material outgassing, the facility was unable to maintain the CQCM temperature setpoint of 80 K QCMs.. The QCMs operating at the warmer temperatures also saturated on occasion due to high levels of condensed matter. Though testing was able to confirm high risk of outgassing contamination for the program, true sticking coefficients could not be determined, available measurements are provided herein.

Alvin Y Huang↗