Dual alloy interface stability

Abstract

Powder metallurgy dual alloy fabrication is applied to combinations of superalloys having a high iron, and low strategic metal content, with standard nickel base superalloys, containing the strategic metals chromium, cobalt, and columbium. The possibility of combining Alloy 901 (12 percent Cr, 36 percent Fe, 0 percent Co, and 0 percent Cb) with turbine disk alloys Rene 95 (13 percent Cr, 8 percent Co, and 4 percent Cb) or low carbon astroloy (L.C.A.; 15 percent Cr, 17 percent Co, and 0 percent Cb) is investigated. Preliminary results for combinations show that a strong interface with rapid diffusion is obtained between alloys and that the standard heat treatments for either alloy may be satisfactory.