Elevated temperature properties of aligned ferrous eutectics

Abstract

Iron base alloys containing aluminum and chromium together with smaller amounts of yttrium and silicon are of interest for high temperature applications. Strengthening an inherently weak but oxidation resistant solid solution matrix with aligned in situ chromium carbides represents an attractive approach to achieving both surface stability and creep resistance at elevated temperatures. Aligned microstructures were produced in alloys of approximately 30 wt % (Cr + Mn), about 3 wt % C and the balance Fe consisting of a gamma matrix and the hexagonal carbide (Cr, Mn, Fe)7C3. The tensile and stress rupture strength to 2000 F of aligned Fe-20 w/t % Cr-10 wt % Mn-3.2 wt % C measured parallel to the carbide reinforcement exceeded those of the strongest iron-nickel superalloys, e.g., CRM-6D developed by Chrysler for automotive turbine application. The cyclic oxidation and sulfidation response of these alloys at elevated temperatures can be markedly improved by aluminum additions.