Development of cast ferrous alloys for Stirling engine application

Abstract

Low cost cast ferrous base alloys that can be used for cylinder and regenerator housing components of the Stirling engine were investigated. The alloys must meet the requirements of high strength and thermal fatigue resistance to approximately 1500 F, compatibility and low permeability with hydrogen, good elevated temperature oxidation/corrosion resistance, and contain a minimum of strategic elements. The phase constituents of over twenty alloy iterations were examined by X-ray diffraction. These alloy candidates were further screened for their tensile and stress rupture strength and surface stability in air at 1450 and 1600 F, respectively. Two alloys, NASAUT 1G (Fe-10Mn-20Cr-1.5C-1.0Si) and NASAUT 4G (Fe-15Mn-12Cr-3Mo-1.5C-1.0Si-1.0Nb), were chosen for more extensive elevated temperature testing. These alloys were found to exhibit nearly equivalent elevated temperature creep strength and oxidation resistance. Silicon present in these alloys at the 1 w/o level permitted the achievement of oxide scale adherence to 1600 F without loss of strength (or ductility) as was noted for equivalent additions of aluminum.