Crack layer morphology and toughness characterization in steels

Abstract

Both the macro studies of crack layer propagation are presented. The crack extension resistance parameter R sub 1 based on the morphological study of microdefects is introduced. Experimental study of the history dependent nature of G sub c supports the representation of G sub c as a product of specific enthalpy of damage (material constant) and R sub 1. The latter accounts for the history dependence. The observation of nonmonotonic crack growth under monotonic changes of J as well as statistical features of the critical energy release rate (variance of G sub c) indicate the validity of the proposed damage characterization.