Thin metal film and multilayers experiment (A0138-3)

Abstract

The sources of degradation of in state of the art and newly developed components and testing the usefulness of the concept of storing experiment samples in dry nitrogen under launch and space vacuum conditions during reentry mission phase were investigated. Ultraviolet (UV) and extreme ultraviolet (EUV) experiments suffer degradations during space missions of even 1 month duration. It is suggested that the degradation is due to condensation of outgassing products, followed by solar induced polymerization, however, penetrating charged particles are also known to produce volume effects. Degradation may also start immediately after manufacturing of the component due to oxidation, moisture, or chemical corrosion by atmospheric constituents such as CO2 and SO2. When the filters are used as windows for gas absorption cells or gas filters, or when they define the instrumental bandwidth by themselves. The effects of mechanical degradation by thermal cycling and/or dust may cause a dramatic impact.