Rubber-toughened polyfunctional epoxies - Brominated vs nonbrominated formulated for graphite composites

Abstract

A new, commercially available, trifunctional epoxy resin (tris-(hydroxyphenyl)-methane triglycidyl ether) was modified with synthetic rubber to increase the impact resistance of epoxy/graphite composites. These composites were reinforced with commercially available satin-weave carbon cloth using two formulations of epoxies (brominated and nonbrominated) containing various amounts of carboxy-terminated butadience acrylonitrile (CTBN) rubber that had been prereacted with epoxy resin. The impact resistance was determined by measuring the interlaminar shear strength of the composites after impact. The mechanical properties, such as flexural strength and modulus at room temperature and at 93 C, were also determined. Measurements were taken of the flammability and glass transition temperature (Tg); and a thermal-gravimetric analysis was made.