Strain rate characterization of unidirectional graphite/epoxy composite

Abstract

For an investigation of problems of composites at high strain rates with dominant wave propagation effects, such as dynamically loaded composite jet engine blades, the longitudinal, transverse, and in-plane shear properties of unidirectional SP 288/AS graphite/epoxy were measured at various strain rates ranging from quasi-static to over 500/s. The test specimens were rings 10.16 cm in diameter, 2.54 cm long, 6 to 8 plies thick, and with fibers at 0, 90, and 10 deg off-axis. Quasi-static testing was conducted in a fixture which applies hydraulic pressure to the ring specimens, and dynamic testing was conducted by applying an internal pressure pulse through a liquid in a special fixture. Dynamic stress-strain curves are presented. For the 0-deg specimens, the modulus increases with strain up to 20 percent of the static value. The modulus and strength increase sharply in the 90-deg rings with strain rate reaching values two to three times the corresponding static rate.