Single cell performance studies on the FE/CR Redox Energy Storage System using mixed reactant solutions at elevated temperature

Abstract

Experimental studies in a 14.5 sq cm single cell system using mixed reactant solutions at 65 C are described. Systems were tested under isothermal conditions, i.e., reactants and the cell were at the same temperature. Charging and discharging performance were evaluated by measuring watt-hour and coulombic efficiencies, voltage-current relationships, hydrogen evolution and membrane resistivity. Watt-hour efficiencies ranged from 86 percent at 43 ma/sq cm to 75 percent at 129 ma/sq cm with corresponding coulombic efficiencies of 92 percent and 97 percent, respectively. Hydrogen evolution was less than 1 percent of the charge coulumbic capacity during charge-discharge cycling. Bismuth amd bismuth-lead catalyzed chromium electrodes maintained reversible performance and low hydrogen evolution under normal and adverse cycling conditions. Reblending of the anode and cathode solutions was successfully demonstrated to compensate for osmotic volume changes. Improved performance was obtained with mixed reactant systems in comparison to the unmixed reactant systems. Previously announced in STAR as N83-25042