Chemical structure of interfaces

Abstract

The interfacial structure of silicon/dielectric and silicon/metal systems is particularly amenable to analysis using a combination of surface spectroscopies together with a variety of chemical structures of Si/SiO2, Si/SiO2Si3N4, Si/Si2N2O, Si/SiO2/Al, and Si/Native Oxide interfaces using high resolution (0.350 eV FWHM) X ray photoelectron spectroscopy. The general structure of these dielectric interfaces entails a monolayer chemical transition layer at the Si/dielectric boundary. Amorphous Si substrates show a wide variety of hydrogenated Si and Si(OH) sub x states that are not observed in thermal oxidation of single crystal material. Extended SiO2 layers greater than 8 A in thickness are shown to be stoichiometric SiO2, but to exhibit a wide variety of local network structures. In the nitrogen containing systems, an approach to stoichiometric oxynitride compounds with interesting impurity and electron trapping properties are seen. In native oxides, substantial topographical nonuniformity in oxide thickness and composition are found. Analysis of metal/oxide interfacial layers is accomplished by analytical removal of the Si substrate by UHV XeF2 dry etching methods.