Hydrogen effects in 001-line oriented nickel-base superalloy single crystals

Abstract

The entry and subsequent interaction of hydrogen on the mechanical properties of the single crystal nickel-base superalloy CMSX-2 has been studied. Significant amounts of hydrogen were introduced by high temperature hydrogen charging in molten salts which led to an increased lattice parameter and microhardness and to a degradation in tensile elongation to failure whose extent scales with the depth of the hydrogenated zone. In this region a fracture mode change from a 111 to a 100 plane type also occurred. The values of the binding energy of hydrogen to solidification voids and the effective hydrogen pressure in the voids were estimated.