Hot piston ring/cylinder liner materials - Selection and evaluation

Abstract

A materials testing program to determine whether automotive Stirling engine efficiency can be improved by locating 'hot piston rings' near the top of the pistons is described. Candidate materials were screened theoretically and experimentally by friction and wear tests. Based on the test results, a cobalt-based alloy, Stellite 6B, was chosen for the piston rings and PS200, which consists of a metal-bonded chromium carbide matrix with dispersed solid lubricants, was chosen as the cylinder coating. Tests of a modified engine and a baseline engine showed that the hot ring did reduce specific fuel consumption by up to 7 percent for some operating conditions and averaged about three percent for all conditions evaluated. Related applications of high-temperature coatings for shaft seals and as backup lubricants for gas bearings are also described.