Damage analysis of a crack layer

Abstract

Damage analysis of a crack layer in polystyrene is carried out by employing optical microscopy and principles of quantitative stereology. The results show that, within the quasistatic phase of crack layer propagation, the average crazing density, along the trailing edge of the active zone, is constant. This is consistent with a self-similarity hypothesis of damage evolution employed by the crack layer theory. The average crazing densities within the active zone and along its trailing edge are found to be practically equal. A layer of constant crazing density, adjacent to the crack planes, accompanies the crack during its quasi-static growth. This suggests that: (1) a certain level of crazing density should be reached, around the crack tip, prior to crack advance; (2) the specific energy, associated with this 'core' of damage, could be considered as a Griffith's type energy. The results are in favor of certain hypothesis adopted by the crack layer theory.