Non-steady state cracking in ceramic matrix composites

Abstract

A micromechanics analytical model based on the consistent shear lag theory is developed for predicting the failure modes in a fiber-reinforced unidirectional ceramic matrix composite. The model accounts for the relatively large matrix stiffness. The fiber and matrix stresses are established as functions of the applied stress, crack geometry, and most importantly, the microstructural properties of the constituents. From the predicted stress, the mode of failure is established based on the point stress criterion. The role of the microstructural properties on the failure mode and ultimate strength is assessed.