Matrix plasticity in SiC/Ti-15-3 composite

Abstract

An experimental method is described which allows for the observation of slip bands due to matrix plasticity in the SiC/Ti-15-3 composite system. A post-test heat treatment and subsequent chemical etch is employed to reveal slip bands in the titanium matrix. Composite specimens of various laminates were examined after tensile testing at room temperature. This method definitively shows that matrix plasticity has occurred in all the laminates investigated and at load/strain levels which were insufficient to cause fiber breakage.