LaRC-TPI 1500 composites fabricated using an aqueous slurry process

Abstract

Unidirectional composites from unsized carbon fiber and LaRC-TPI matrix material were fabricated using 'high flow' and'medium flow' grades of the LaRC-TPI 1500 series of polyimides. Prepreg was drum-wound from a slurry composed of the polyimide powder dispersed in an aqueous solution of LaRC-TPI poly(amide acid). The poly(amide acid) was found to be an effective binding agent in the prepregging process. Composite short beam shear and flexure properties were measured at room and elevated temperatures (to 177 C) with both dry and moisture-saturated specimens. The mechanical properties observed for composites fabricated from the high and medium flow materials were virtually identical. Additionally, double cantilever beam measurements showed nearly equivalent fracture toughness for the two composite materials.