Thermal imaging of graphite/epoxy composite samples with fabricated defects

Abstract

Consideration is given to a thermal inspection system for quickly inspecting large area composites for increased reliability and maintainability of helicopters resulting from improved quality assurance manufacturing. The infrared camera/image processor-based inspection system was used to image defects in composites. Noncontacting and single-sided measurements were performed on graphite/epoxy samples with fiber volume fraction variations, fabricated porosity, impact damage, and inclusions in incurred lay ups. These defects were imaged by determining the variations in the cooling rates caused by differences in through ply thermal diffusivity. Attention is also given to the system's sensitivity to measuring the defects due to sample thickness.