Tension, Compression, and Bend Properties for Sic/RBSN Composites

Abstract

The room-temperature tension, compression, and bend properties of unidirectional SiC fiber-reinforced reaction-bonded silicon nitride composites (SiC/RBSN) have been investigated. The effects of fiber content on the modulus, first matrix cracking strength, and ultimate strength properties were determined. In tension, composites with greater than 8-percent fiber content showed strain capability beyond matrix fracture and fiber-dominated ultimate strength. In compression, the composites displayed essentially elastic behavior, and matrix-dominated ultimate strength. For both deformation modes, most mechanical properties increased with fiber content. In bend, the modulus, strength properties, and failure modes of the composites were influenced by span-to-thickness ratio.