Titanium honeycomb panel testing

Abstract

The paper describes the procedures of thermal mechanical tests carried out at the NASA Dryden Flight Research Facility on two tianium honeycomb wing panels bonded using liquid interface diffusion (LID) technique, and presents the results of these tests. The 58.4 cm square panels consisted of two 0.152-cm-thick Ti 6-2-4-2 face sheets LID-bonded to a 1.9-cm-thick honeycomb core, with bearing plates fastened to the perimeter of the upper and the lower panel surfaces. The panels were instrumented with sensors for measuring surface temperature, strain, and deflections to 315 C and 482 C. Thermal stress levels representative of those encountered during aerodynamic heating were produced by heating the upper panel surface and restraining all four edges. After more than 100 thermal cycles from room temperature to 315 C and 50 cycles from room temperature to 482 C, no significant structural degradation was detected in the panels.