High voltage thermally diffused p(+)n solar cells

Abstract

The possibility of fabricating thermally diffused p(+)n InP solar-cells with high open-circuit voltage without sacrificing the short circuit current is discussed. The p(+)n InP junctions were formed by Cd and Zn diffusion through a 3-5-nm-thick anodic or chemical phosphorus-rich oxide cap layer grown on n:InP:S (with ND-NA = 3.5 x 10 exp 16 and 4.5 x 10 exp 17/cu cm) Czochralski LEC-grown substrates. After thinning the emitter from its initial thickness of 1 to 2.5 micron down to 0.06-0.15 micron, the maximum efficiency was found when the emitter was 0.2 to 0.3 micron thick. Typical AM0, 25 C values of 854-860 mV were achieved for Voc, Jsc values were from 25.9 to 29.1 mA/sq cm using only the P-rich passivating layer left after the thinning process as an antireflection coating.