Solidification kinetics and metastable phase formation in binary Ti-Al

Abstract

Electromagnetic levitation was used to solidify near-equiatomic alloys of Ti-Al at various bulk undercoolings. Detailed thermal histories were acquired during experiments using optical pyrometry with sampling rates as fast as 500 KHz. Solidification and other high-temperature transformation pathways were deduced from the thermal data and microstructural analysis. Recalescence rise times were employed to determine semiquantitative primary solidification kinetics for the different phases. Primary beta solidification was observed at compositions well into the equilibrium alpha regime; this is presented as part of a near-equiatomic nucleation domain diagram that shows the primary solidification phase that results for each combination of nucleation temperature and composition. Solidification kinetics are faster for primary beta than they are for primary alpha. For undercoolings less than about 150 K, the primary solidification kinetics are about an order of magnitude slower for gamma than for alpha.