Liquidus Temperatures and Solidification Behavior in the Copper-Niobium System

Abstract

The copper-niobium phase diagram has been under active debate; thus, a corroboratory experimental study is needed. In this investigation, the melts of Cu-Nb alloys at compositions ranging from 5 to 86 wt pct Nb were processed in different environments and solidified at relatively low cooling rates of 50 to 75 C/s to determine liquidus temperatures and to study solidification behavior. For all samples processed under very clean conditions, only Nb dendrites in a Cu matrix were observed; while in the presence of oxygen impurities the alloys containing 5 to 35 wt pct Nb exhibited microstructure of Nb-rich spheroids and Nb dendrites in the Cu matrix. The results obtained from clean conditions are in fair agreement with the Cu-Nb phase diagram having an S-shaped, near-horizontal appearance of the liquidus. The formation of Nb- rich droplets at slow cooling rates is discussed in terms of a stable liquid miscibility gap induced by oxygen.