Cr(+2) Diffusion Doping in ZnSe

Abstract

Chromium doped zinc selenides crystals have recently been demonstrated to be a promising material for near-IR room temperature tunable lasers which has an emission range of 2-3 pm. In this study, a new diffusion doping process has been developed for incorporation of Cr(+2) ion into ZnSe wafers. This process has been successfully performed under isothermal conditions, at temperatures above 800 degrees Celsius. Concentrations in excess of 10(exp 19) Cr(+2) ions/cu cm, an order of magnitude larger than previously reported in melt grown ZnSe material, have been obtained. The diffusivity was estimated to be about 10-* sq cm/sec using a classical diffusion model. Resistivity was derived from current-voltage measurements and in the 107-10(exp 16) Ohms-cm and increased as function of Cr concentration.