Transport Modeling for Metallic Electrode: Semiconducting Nanotube Systems

Abstract

Recently, current-voltage (I-V) characteristics have been reported by Collins et al. for a system with a scanning tunneling microscope (STM) tip and a carbon nanotube. The STM tip was driven forward into a film of many entangled nanotubes on a substrate, and then was retracted, so that one of nanotubes bridged the STM and the film. I-V characteristics had two different patterns for different heights. One showed large dI/ dV with V greater than 0, small dI/dV with V less than 0, and I = 0 near V = 0 (type-I), while the other showed rectification, i.e., I does not equal 0 only with V less than 0 (type-II), with the tip grounded. We propose a physical mechanism to explain the observed I-V patterns. We consider that the observed characteristics strongly reflected the nature of the tip (metal) - nanotube (semiconductor) contact. The other end of the nanotube was entangled well in the film, and simply provided a good Ohmic contact. We will argue that there are two different contact modes: vacuum gap and touching modes, depending on the presence or absence of a tiny vacuum gap d approx. 0.1 - 0.2 nm at the junction. These modes may be related to physisorption and chemisorption, respectively. Once admitting their existence, it is naturally shown that I-V characteristics are type-I in the vacuum gap mode, and type-II in the touching mode. We argue that the nanotube had to be an n-type semiconductor judging from the I-V characteristics, contrary to often observed p-type in the transistor applications, where p-type is probably due to the oxidation in air or the trapped charges in the silicon dioxide. Additional information is contained in the original extended abstract.