Micro-Cracking Detection in Laminated Composites

Abstract

Porosity and fatigue cracking are two critical factors that affect the performance and safety of cryogenic fuel tanks and feedlines made from unlined laminated or weaved carbon/epoxy materials. This paper presents the experiments to induce fatigue cracking of laminated composites through thermal cycling as well as the feasibility of using Thermography and Ultrasound Spectroscopy technology (UT) to detect and measure such micro-cracking. Carbon/epoxy laminated composite panels were built and cut into strips. These specimens were partially submerged in liquid nitrogen while subjected to various loads on a test machine. Edges of some specimens were polished and etched to determine the degree of micro-cracking. The rest of specimens were then examined with Thermography and Ultrasound Spectroscopy NDE systems to investigate the feasibility of finding such micro-cracking in the laminated composites. Thermography is utilized to determine changes in thermal diffusivity. The degree of cracking may reduce the apparent thermal diffusivity and therefore change the thermal response on the surface. Thermography testing was conducted on a group of specimens where it is desired to have some correlation between the predetermined stress and the thermography data. Ultrasound Spectroscopy was used to determine peak changes between the pre-stressed and stressed samples. Data from the inspections were analyzed and the results are presented in this paper.