Preparation and Characterization of Polyimide Nanocomposites

Abstract

Many properties of polymeric materials can be enhanced by dispersing small quantities of clay nanocomposites throughout the polymer. Among the enhancements are increases in modulus and resistance to erosion by atomic oxygen and reductions in thermal expansivity, gas permeability, and flammability. To achieve the full extent of enhancement with these polymer-clay nanocomposites, the clay nanoparticles, which have thicknesses of only one-to-several nanometers and lengths and widths of hundreds of nanometers to micrometers, must be exfoliated one from another and then individually dispersed throughout the polymer. This dispersion is achieved only after alkali metal cations (usually Na(+)) that reside on the surfaces of the nanoparticles have been replaced by organocations (typically a quaternary amine cation). This renders the surface of the nanoparticle a more hospitable interface for the organic polymer matrix. Following the cation exchange, the organic clay is either mixed directly into the polymer or is dispersed in monomer which is later polymerized around the nanoparticle.