Damage Accumulation in SiC/SiC Composites with 3D Architecture

Abstract

Matrix cracking in Sic fiber reinforced, melt-infiltrated Sic composites with 3D orthogonal architectures was determined for specimens tested in tension at room temperature. Acoustic emission (AE) was used to monitor the matrix cracking activity and was later confirmed by microscopic examination of specimens that had failed. Exact location of AE demonstrated that initial cracking occurred in the matrix rich regions when a large z-direction fiber bundle was used. For specimens with large z-direction fiber tows, the earliest matrix cracking could occur at half the stress for standard 2D woven composites with similar constituents.