Low-Cost, Large C-SiC Blisk Fabrication

Abstract

C-SiC composites offer unique properties for propulsion applications. However, fabrication of low-cost, thick, large scale C-SiC disk for integrally bladed disk (blisk) applications has not been established yet. MER has demonstrated a new process to address this issue. Polymer-based processing was employed for interfacial coatings, consolidation and densification. Up to 40" O.C., 2" thick C-SiC composite processing was established, yielding in excess of 1.8 g/cu cm density. Computer tomography (CT) scans on the 40" O.D., 2" thick C-SiC disk showed no visible delamination, and good density uniformity. Stress-rupture testing in air was conducted at 2200 F, 2400 F and 2550 F.