Atomic Oxygen Energy in Low Frequency Hyperthermal Plasma Ashers

Banks, Bruce A.; Miller, Sharon K R.; Kneubel, Christian A.

Home/Archive/NASA NTRS

NASA NTRS · 20150000318

Atomic Oxygen Energy in Low Frequency Hyperthermal Plasma Ashers

Banks, Bruce A.·Miller, Sharon K R.·Kneubel, Christian A.

View original source ↗Export metadata ↓

Abstract

Experimental and analytical analysis of the atomic oxygen erosion of pyrolytic graphite as well as Monte Carlo computational modeling of the erosion of Kapton H (DuPont, Wilmington, DE) polyimide was performed to determine the hyperthermal energy of low frequency (30 to 35 kHz) plasma ashers operating on air. It was concluded that hyperthermal energies in the range of 0.3 to 0.9 eV are produced in the low frequency air plasmas which results in texturing similar to that in low Earth orbit (LEO). Monte Carlo computational modeling also indicated that such low energy directed ions are fully capable of producing the experimentally observed textured surfaces in low frequency plasmas.

Explore related subjects

Oxygen atoms Plasmas (physics)

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Banks, Bruce A., Miller, Sharon K R., Kneubel, Christian A.. 2014-11-01. Atomic Oxygen Energy in Low Frequency Hyperthermal Plasma Ashers. https://ntrs.nasa.gov/citations/20150000318

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS2018

Atomic Oxygen Environments, Effects, and Mitigation

Atomic oxygen is the most predominant specie in low Earth orbit (LEO) and is contained in the upper atmosphere of many other planetary bodies. Formed by photo-dissociation of molecular oxygen, it is highly reactive and energetic enough to break chemical bonds on the surface of many materials and react with them to form either stable or volatile oxides. The extent of the damage for spacecraft depends a lot on how much atomic oxygen arrives at the surface, the energy of the atoms, the reactivity of the material that is exposed to it and other constituents in the atmosphere. Oxide formation can result in shrinkage, cracking, or erosion which can also result in changes in optical, thermal, or mechanical properties of the materials exposed. The extent of the reaction can be affected by mechanical loading, temperature, and other environmental components such as ultraviolet radiation or charged particles. Atomic oxygen generally causes a surface reaction, but it can scatter under coatings and into crevices causing oxidation much farther into a spacecraft surface or structure than would be expected. Atomic oxygen effects for LEO atomic oxygen compared to atomic oxygen effects in a Mars environment, effects atomic oxygen can have on typical spacecraft materials, and mitigation techniques will be presented.

Oxygen atoms↗

NASA NTRS2014

Comparison of the Results of MISSE 6 Atomic Oxygen Erosion Yields of Layered Kapton H Films with Monte Carlo Computational Predictions

A space experiment flown as part of the Materials International Space Station Experiment 6B (MISSE 6B) was designed to compare the atomic oxygen erosion yield (Ey) of layers of Kapton H polyimide with no spacers between layers with that of layers of Kapton H with spacers between layers. The results were compared to a solid Kapton H (DuPont, Wilmington, DE) sample. Monte Carlo computational modeling was performed to optimize atomic oxygen interaction parameter values to match the results of both the MISSE 6B multilayer experiment and the undercut erosion profile from a crack defect in an aluminized Kapton H sample flown on the Long Duration Exposure Facility (LDEF). The Monte Carlo modeling produced credible agreement with space results of increased Ey for all samples with spacers as well as predicting the space-observed enhancement in erosion near the edges of samples due to scattering from the beveled edges of the sample holders.

Oxygen atoms↗